NOTICE

Forums are temporarily disabled while we are working on a new login procedure.

When migrating the old forums over to our new forums we were unable to retain the identity of the authors, so the old posts will show up as "anonymous". All NEW posts will show up credited to their authors. So please participate and share knowledge just as you have in the past.

You must log in if you are an existing user or register if you are a new user in order to contribute to the discussions.

Discussion Forums - The Hendrix Group
HomeHomeDiscussionsDiscussionsGeneral Corrosi...General Corrosi...Stress corrosion on LTCSStress corrosion on LTCS
Previous
 
Next
New Post
2/16/2009 9:00 AM
 
Hi, I have a query regarding possible stress corrosion of low temp carbon steel with liquid ammonia. some of the weld specs stongly recommend PWHT to control hardness while some do not. i would like to know 1. how critical is SCC on LTCS with liquid ammonia (in presence of min 1% water) 2. How important is hardness that any repair on ammonia storage tank and pipework shall require PWHT regards regards
 
New Post
2/17/2009 9:00 AM
 
Bigpond In presence of water ( water =0.5% or above) SCC trend is inhibited in liquid ammonia service. For LT carbon steel - if hardness as welded or in HAZ or in parent plate or pipe exceeds 210 BHN ( approx: 21 HRc) it is advisable to carry PWHT to limit the trend of SCC in ammonia service. For tanks > 20 mm wall thickness, if repair welded hardness is > 210 BHN (approx: 21 HRc) then depending on hardness and code regulations PWHT may be needed. Hope this helps C.V.Srinivasan Nishi Engineers Pvt Ltd India Feb 17, 2009 E-mail: nishi@vsnl.com >Hi, >I have a query regarding possible stress corrosion of low >temp carbon steel with liquid ammonia. some of the weld >specs stongly recommend PWHT to control hardness while some >do not. i would like to know >1. how critical is SCC on LTCS with liquid ammonia (in >presence of min 1% water) >2. How important is hardness that any repair on ammonia >storage tank and pipework shall require PWHT > >regards >regards
 
Previous
 
Next
HomeHomeDiscussionsDiscussionsGeneral Corrosi...General Corrosi...Stress corrosion on LTCSStress corrosion on LTCS


  

News

With a little delay, our Calculation of Ammonium Salt Deposition Temperatures...read more
Our sulfidic corrosion calculators are now available at hghouston.com/calcula...read more

Stay Current

Sign up for our quarterly newsletter

covering updates on corrosion

Sign Up