NOTICE

Forums are temporarily disabled while we are working on a new login procedure.

When migrating the old forums over to our new forums we were unable to retain the identity of the authors, so the old posts will show up as "anonymous". All NEW posts will show up credited to their authors. So please participate and share knowledge just as you have in the past.

You must log in if you are an existing user or register if you are a new user in order to contribute to the discussions.

Discussion Forums - The Hendrix Group
HomeHomeDiscussionsDiscussionsGeneral Corrosi...General Corrosi...Fired heater stack corrosionFired heater stack corrosion
Previous
 
Next
New Post
3/10/2005 9:00 AM
 
We are facing a repetitive corrosion in a fired heater stack. This heater is a balanced draft heater with Flue gas temperature of 195 deg C , against dew point of 150 deg C. What could be the reasons for the same,also what causes corrosion of refractory , and how it can be corrected. Thanking you in anticipation please.
 
New Post
3/10/2005 9:00 AM
 
Sgoel: It is not clear to us whether corrosion (deterioration) is occurring to a metal substrate or to an insulating refractory lining. It is also not clear why a refractory lining is in use at 195C. You might also elaborate on the makeup of the combustion gases. David Hendrix The Hendrix Group Inc.
 
New Post
3/10/2005 9:00 AM
 
David Thanks a lot for reply. The flue gas is containing about 74% N2, 12% CO2, 10.2 % H2O, 3.5 % O2 and 0.3 % SO2. Corrosion is taking place on the metal. But the problem starts with degradation of refractory, causing corrosion flue gases to get cooled. This results in dew point corrosion of steel. Hope I made myself clear. Best Regards Shashank Goel
 
New Post
3/23/2005 9:00 AM
 
Sgoel: Your metal substrate corrosion is most probably occurring due to dew point corrosion, with the condensate pH being depressed by CO2. Hope this helps! David Hendrix The Hendrix Group Inc.
 
New Post
3/23/2005 9:00 AM
 
Goel As David says I suppose with that Flue gas temperature of 195 deg C you don’t need a refractory lining. As the refractory act as an insulating it will force the dew point formation underneath the refractory and you will get corrosion on stack plates. If you need to conserve that temperature of 195 deg C why not to put a thermal insulation (rock wool blankets plus aluminium weatherproofing)outside of the stack? Regards Luis Marques
 
Previous
 
Next
HomeHomeDiscussionsDiscussionsGeneral Corrosi...General Corrosi...Fired heater stack corrosionFired heater stack corrosion


  

News

With a little delay, our Calculation of Ammonium Salt Deposition Temperatures...read more
Our sulfidic corrosion calculators are now available at hghouston.com/calcula...read more

Stay Current

Sign up for our quarterly newsletter

covering updates on corrosion

Sign Up